Preparation of zinc oxide/reduced graphene oxide composite material used in light applications, involves preparing graphite oxide, dissolving polyvinyl alcohol in water, adding soluble zinc salt, magnetically stirring, freezing and drying.

JIN J, LIU X

Producing composite composition of zinc oxide and graphene oxide, comprises e.g. mixing zinc chloride and graphene oxide obtained by mixing e.g. sodium nitrate and sulfuric acid, and treating with water and sodium hydroxide solution.

JO H H, CHOI H K, JEON M H

Preparing three-dimensional graphene-zinc oxide composite nano paper, comprises printing design pattern on chromatographic paper, melting wax, then dissolving Hummers synthesized graphene oxide, and preparing graphene paper.

YANG H, ZHANG Y, HU M, LI L, YAN M, GE S, YU J

Preparation of self-assembled graphene inline growth nano-rod array composite film, involves immersing metal zinc sheet in graphene oxide solution, reacting, removing, and drying to obtain zinc sheet self-assembled reduced graphene film.

FANG Y, ZHONG Y, YANG S, ZHANG S

Preparing reduced graphene oxide/zinc oxide hollow microspheres comprises e.g. dissolving zinc acetate dihydrate in anhydrous ethanol, stirring and adding ethanolamine and stirring, centrifugal collecting solid product, washing and drying.

MA Z, SONG P, WANG Q, YANG Z, ZHONG X

Preparing graphene-based thin-film laminate used in e.g. transistor, comprises conducting cycle having e.g. contacting surface of graphene onto substrate with non-metal precursor gas and activating surface of graphene with plasma N times.

PARK C, CHO S, SEO S, SHIN S, KIM T, KIM S, PIAO Z, SEO S A, SHEN Z, PARK C H, CHO S M, SHIN S M, KIM T K, KIM S Y

Preparation of three-dimensional-hierarchical porous graphene aerogel for energy storage material, involves adding metal oxide to graphene oxide dispersion, stirring, hydrothermally reacting, reducing and treating with acid.

HUI K N

Preparing zinc oxide quantum dot/graphene-based composite material comprises uniformly mixing natural graphite, stirring, diluting, stirring, washing, dialyzing, drying, dripping, reacting, centrifuging, washing, filtering and drying.

WANG B, LIN W, WAN J, PENG Z, HU Z

Polydiallyldimethylammonium chloride modified graphene oxide-zinc oxide composite material comprises spindle-shaped thin two-dimensional material that is loaded with zinc oxide material under transmission electronic microscope.

ZHANG J, FAN Y, ZHANG L, NIE K, CHENG Y, ZHU H, CAI Y, MI C

Producing reduced graphene oxide involves mixing of lumen output particle with aqueous solution of graphene oxide and exposing light, which corresponds to absorption wavelength, where lumen output particle is metal nanoparticles.

PARK H Y, PARK J H, YOO G W