Thick-coated modified aqueous acrylic acid heavy anti-corrosion paint comprises e.g. epoxy resin modified aqueous acrylic acid emulsion, 0deionized water, ethylenediamine graft modified graphene, pigment filler, antifoaming agent, thickening agent, film-forming auxiliary agent and pH regulator.

DUAN S, SHANG N, KANG S, DING C, CUI C, GUO X, WANG L, HAN Z, SHI J

Protective coating for repairing metal surface damage, is set on the metal material substrate damage area surface, comprising a resin material layer from inside to outside in turn set on surface of the metal material substrate damage area.

WANG L, ZHAO Q, WU Y, ZHAO W

Preparing Teflon corrugated pipe internal crimping joint comprises using 304 stainless steel processing to make withholding joints and coating crimping joint surface with corrosion-resistant modified polyperfluoroethylene propylene coating.

WANG W, WANG L, LI S

Anticorrosive coating includes epoxy resin E-20, butanediol glycidyl ether, titanium dioxide, silicon powder, thinner, antiseptic composition, butyl acetate, curing agent, bentonite, m-phenylenediamine, and aluminum tripolyphosphate.

DENG W, YANG D, WANG L

Preparing low-temperature resistant, stretch-resistant and anticorrosive coating, comprises e.g. dispersing graphite oxide in deionized water, dissolving polyetheramine, refluxing, and adding black dispersion to acrylic resin emulsion.

MA J, ZHANG L, SUN D, WEI K, LIU N, HUANG B, ZHANG H, YANG S, ZHU S, WANG L, CHU J

Preparing high temperature resistant functionalized graphene modified aqueous polyurethane useful as transfer aluminized coating on food comprises e.g. adding polyester diol, diisocyanate, methacrylate monomers into drying reactor.

LAI X, QIN Y, WANG L, ZENG Q, ZHAO Y, LIU M, ZHAO X

Hydroxyl-terminated hyperbranched poly(amine-ester) modified graphene oxide/epoxy resin nanocomposite coating to prevent from corroded, comprises hydroxyl-terminated hyperbranched poly(amine-ester) modified graphene oxide and epoxy resin.

SUN R, HAO Y, ZHOU Y, WANG L, ZHOU H, LIU J, SHI Z, ZHAO H, CHEN Z, CHEN Y, YU G, GAO F