Nanocomposite graphene modified mine supporting roller pipe material comprises e.g. nano super-conductive carbon black, polyethylene and acrylic acid graft copolymer, graphene, micropowder graphite, ultrafine microcapsule red phosphorus, zinc stearate and ultra-high molecular weight polyethylene.

QI J, LI M

Preparing light-weight composite material with excellent mechanical properties at high temperature useful in automobile, by e.g. processing chopped carbon fiber at a high temperature in an ammonia atmosphere, mixing aminated carbon fiber and oxidized carbon modifier, kneading, filtering and molding.

ZHAO L, WANG C, HAN F

Dispersing graphene material in thermoplastic to form a masterbatch for use in e.g., bottles and textiles by loading thermoplastic with specific initial intrinsic viscosity (IV) into extruder or continuous mixer and adjusting IV of mixture.

FUKUSHIMA H, SHABAFROOZ V

Reinforced wear-resistant PE drainage pipe for trenchless construction, comprises high density polyethylene, linear low density polyethylene, nano graphene, polyaniline modified bentonite and titanate coupling agent.

LIU J, CAO C, JIANG F, ZHANG J, ZHOU M, GU Y, ZHU Q

Preparing plastic comprises dispersing graphene oxide in a mixed solution and ultrasonically stirring, and mixing the mixed solution containing graphene oxide and polyethylene, uniformly stirring and volatilizing in the solvent mixture.

DUAN H

Graphene-based poly(vinyl chloride) pipe contains poly(vinyl chloride), phenolic resin, flame-retardant masterbatch, ultra-high-molecular-weight polyethylene, graphene, butyl stearate, butanol, pentaerythritol stearate and heat stabilizer.

HUANG Y, HUANG Z

Graphene-modified rubber material for three dimensional printing involves washing waste rubber, drying, crushing, sieving to obtain rubber powder, adding surfactant to obtain activated rubber powder and crushing graphene to obtain powder.

ZHONG Z

Carbon fiber-reinforced polyoxymethylene composite material comprises polyoxymethylene, carbon fiber, butyl stearate, melamine, bis(octadecanol) ester, calcium carbonate, silane coupling agent, graphene oxide and nanosilica.

ZHU Z

Carbon fiber-reinforced polyoxymethylene composite material comprises polyoxymethylene, carbon fiber, bis(dodecanol ester), homopolyamide, n-butyl stearate, calcined kaolin, silane coupling agent, graphene oxide, and nanosilica.

ZHU Z

Carbon fiber-reinforced polyformaldehyde composite material contains polyoxymethylene, carbon fibers, molybdenum disulfide, stearamide, silicone oil, antioxidant, nano white carbon black, copolyamide, graphene oxide and nano silica.

ZHU Z