Graphene in-situ modified polyimide film is prepared by polycondensation of graphene grafted with aminosiloxane on the surface, diamine and dianhydride and forming into film.

XU Z, LIU G, ZHANG Q

Silica and graphene composite powder material useful as reinforcing agent for high molecular polymers, reinforcing styrene butadiene rubber, improving processing property of materials and ensuring excellent antistatic property of materials.

ZHANG Q, ZHANG Y, WANG C

Friction reducing graphene comprises graphene, molybdenum boride, ethoxylation alkyl ammonium sulfate saturated, stearamide, methyl methacrylate, acrylic acid, ammonium persulfate, silane coupling agent kh550, and sucrose isobutyrate.

ZHANG Q

Polypyrrole composite graphene comprises pyrrole, ammonium persulfate, graphene, sucrose acetate isobutyrate, ascorbic acid, 1,6-hexanediol diacrylate, polymethylhydrosiloxane, and platinum catalyst.

ZHANG Q

Preparation of functionalized graphene-carbon nanotube reinforced epoxy resin composite involves mixing functionalized graphene-carbon nanotubes component, and component formed of nano alumina, adding curing agent and molding.

ZHANG Q

Flame-retardant high-temperature nylon graphene composite material comprises e.g. nylon salt, graphene oxide, expanded graphite, silane coupling agent KH560, nano-carbon sol, mica, blocking agent, 6-aminocaproic acid and deionized water.

ZHENG J, ZHANG Q, LI W

Wear- and high temperature- resistant nylon-based composite functional materials comprise e.g. nylon salt, graphene oxide, brucite fibers, expanded graphite, silane coupling agent KH560, nano-carbon sol, nano-titanium dioxide and talc.

ZHENG J, ZHANG Q, LI W

Modified graphene/styrene-butadiene rubber composite comprises vulcanization accelerator, antioxidant and coupling agent including e.g. aluminate coupling agent, rare earth coupling agent, silane coupling agent or titanate coupling agent.

WU Q, ZHAI B, WU T, ZHANG Q

Preparation of functionalized graphene/phenolic resin used for friction material, involves uniformly mixing phenol and formaldehyde, adding functionalized graphene oxide, ultrasonically treating, adding catalyst, heating and reacting.

XIA T, GUO F, DAN X, HUANG J, ZHANG Q, SUN Z

Preparing graphene-based composite ballistic-resistant material useful for e.g. vehicles, comprises e.g. performing graphene or graphene oxide coupling treatment by organic chromium, silane, titanate coupling agent or aluminum acid compound.

WANG K, ZHANG H, ZHANG Q, ZHANG Y, YANG B, ZHANG T, SUN Y, LI X, XI F, DAN R