Graphene/epoxy composite wave-absorbing material used in graphene/epoxy composite coating, comprises epoxy resin and radial graphene clusters that are dispersed in epoxy resin.

LIU L, GAO L, LI Q, LI W, GUO Y, ZHANG H

High stacking degree graphene modification based high thermal conductivity carbon plastic alloy useful in industrial heat dissipation, illumination heat dissipation and heat dissipation of electronic devices, comprises e.g. coupling agent.

HUANG W, ZHAO L, LIN L, SUN D, ZHANG B, LIN J

Preparing high-strength graphene-based thermally conductive film comprises e.g. heating graphene, incubating, collecting lower graphene precipitate, drying to obtain modified graphene, casting, paving mixed solution on mold plate and drying.

YUAN J

Epoxy glass fiber cloth laminate is prepared by coating glass fiber cloth with mixed adhesive comprising epoxy resin, curing agent, accelerator, solvent, and graphene dispersion, laminating and curing.

DU W, LU H, LIU B, HONG J, TAO C

Epoxy resin composite material used as electronic packaging material, comprises graphene, curing agent and epoxy resin, and sufficiently disperse graphene in epoxy resin by improving thermal conductivity of epoxy resin.

ZOU L, ZHANG Z

Preparing silicon carbide/graphene oxide composite modified epoxy resin involves preparing an aqueous dispersion of graphene oxide, adding a silane coupling agent and silicon carbide into it, and heating it to carry out reaction.

WU L, YANG G, WANG G, WANG X, LI M

Preparing thermally conductive porous graphene-epoxy composite material comprises slice grinding graphite, reacting, carrying out ultrasonic oscillation, washing, grinding, crushing, pouring, stirring, allowing to stand and cooling.

TANG G

Fluorescent conductive nano composite material contains epoxy resin, silicone rubber, right-handed polylactic acid type polyurethane elastomer, nanocrystalline cellulose particles, carbon nanotubes, graphene, and coupling agent.

LI D

Preparing graphene or graphite film/carbon fiber resin-based composite material laminated plate by preparing mesh-shaped graphene or graphite film prepreg, then with unidirectional carbon fiber prepreg and subjecting to Z-pins treatment.

BAI S, ZHANG Y

Preparation of lightweight graphene nylon composite material, involves mixing foamed casting nylon, graphene, abrasion agent, thermally conductive filler, lubricating dispersant and additive, adding to extruder, melting and extruding.

LIN Q