Preparing flexible graphite grounding conductor material comprises e.g. mixing resin, carbon forming agent, conductive material, stirring to form carbon resin, impregnating carbon material with carbon-forming resin, paving, stacking tape.

FAN M, HE H, TAN B, WANG X, TONG X, DAI M, LI Z

Hollow particles used for heat-dissipation fluid composition, comprise inorganic particle layer comprising ceramic particles and conductive carbon-based particles as spherical hollow particles and having empty inner space inside, and polymer coating layer.

KWON K A, CHUN M S, KIM D Y, SEOK C M, KIM D, QUAN W, QUAN J

Use of silicon carbide whisker modified with fluorosilane coupling agent oligomer, for improving thermal conductivity of silicon carbide ceramic plate used for substrates of high-brightness LED light source.

ZHANG X, LING J, PAN T, BAI W

Refractory material for steel making steel ladle application area, comprises reduced graphene oxide, flaky graphite, aluminum metal powder, silicon metal powder, liquid resol resin, and boron carbide.

GHOSH G, BISWAS S, CHOUDHARY S K, PAL A R, DEBASISH S, SARATH C K, SARKAR D, CHANDRA S K

Elastic heat spreader film used for forming structural component, comprises graphitic film comprising graphitic crystals, and having preset thermal conductivity, electroconductivity and physical density, and elastomer or rubber.

LIN Y, JANG B Z, ZHANG B, JEAN B

Preparing bending-resistant composite radiating film comprises e.g. taking graphite oxide aqueous solution, firstly adding radiating filler, stirring uniformly, then adding emulsifier and stirring until emulsifier is completely dissolved.

LIN Y, LI X, ZHANG Y, YANG X

Making mixture for concrete comprises providing carbon nanomaterial having carbon nanoparticles, wetting and dispersing carbon nanomaterial in liquid organic solvent/compound mixture, and selecting the mixture to perform e.g. additional function in particular type of concrete.

LARSEN A G, FULTON J L, HULBERT D M, SCHMITT G E, SHIMON C

Ceramic dielectric material comprises barium titanate base material and coating material, and is prepared by dissolving coating material in toluene, adding base material dispersed in deionized water, ultrasonically-processing and distilling.

LIU Z, MA M, CHU X, LUO Y, ZHANG J