Preparing graphene composite material involves preparing dopamine hydrochloric acid buffer solution, adjusting pH value, dipping salix cellulose dipped in the buffer solution at room temperature, washing by de-ionized water.

QIAN Y, ZHAO B

Preparing graphene-silk three-dimensional porous nanocomposite involves dispersing sodium alginate in deionized water at a normal temperature, adding polyamidoamine (PAMAM) solution, reacting, and repeatedly washing with distilled water.

QIAN Y, ZHAO B

Preparing silk-salix graphene-nano composite material useful for absorbing materials, photocatalysis and bio-material fields comprises soaking the salix cellulose in sodium hydroxide solution, neutralizing, drying and redispersing in water.

QIAN Y, ZHAO B

Preparing cellulose/silk magnetic porous composite material based on graphene/silver nano wire comprises e.g. soaking cellulose in dopamine tris-hydrochloric acid buffer, adding silver nano wire and amino terminated hyperbranched polymer.

ZHAO B

Preparation of graphene oxide-silksalix nano composite material involves mixing salix cellulose into sodium hydroxide solution at normal temperature, washing with deionized water, drying, redispersing in water, and mixing liquor.

QIAN Y, ZHAO B

Preparation of graphene/silk protein/Salix nanocomposite for e.g. sewage treatment, involves adding sodium periodate modified Salix cellulose, immersing composite material in graphene oxide solution, adding reducing agent.

QIAN Y, ZHAO B

Preparation of silk fibroin-sodium alginate porous composite material loaded with graphene and silver nanowires for e.g. biomaterial, involves immersing composite material in hyperbranched polymer modified silver nanowires solution.

ZHAO B

Preparing graphene oxide-coated silk composite material involves preparing dopamine tris-hydrochloric acid buffer to adjust pH value, soaking Salix Cellulose in buffer at room temperature, then repeated washing with deionized water.

QIAN Y, ZHAO B

Preparing graphene oxide-sodium alginate magnetic composite material comprises e.g. dispersing sodium alginate in deionized water, dissolving silk protein in deionized water, adding ferric salt solution into silk protein solution and drying.

QIAN Y, ZHAO B

Preparing graphene oxide-silk fibroin-amphoteric cellulose composite material comprises placing the cellulose in sodium hydroxide solution, reacting, washing repeatedly with deionized water until neutral.

ZHAO B