Preparing substrate of multiple graphene films involve subjecting metal substrate to high temperature annealing, cooling metal substrate to room temperature, coating layer of carbon solution on metal substrate, and solidifying solution.

GAO X, JIANG H, LI Z, SHI H

Light heat-radiation film with sandwich structure, comprises aluminum foil with micropores as middle layer provided between graphene heat-radiation films.

LIU L

Preparation aluminum and aluminum alloy surface coating involves preparing graphite oxide to graphene sheet material, where graphene oxide sheet is dispersed in deionized water to obtain aqueous solution of graphene oxide.

CHEN P, WANG Y

Synthesizing reduced graphene oxide on a substrate from seedlac, comprises preparing the seedlac solution in alcohol having specified carbons, dipping the substrate into the solution, and heating the substrate which is a metallic sheet.

SHYAM K C, MANISH K B, TAPAN K R, SUMITESH D, RANJAN K S, YASHABANTA N S, ASHIT K P, VIKAS C S, CHOUDHARY S K, BHADU M K, ROUT T K, DAS S, SAHU R K, SINGHBABU Y N, PRAMANICK A K, SRIVASTAVA V C

Preparing graphene, comprises e.g. placing sheet-type metal substrate in a reaction chamber, contacting with carbon source material, and irradiating one side surface of sheet-type metal substrate by using laser beam, and irradiating again.

GAO J, LI B, JIANG J, LIU R, TENG Y, WANG Q

Producing graphene film coated titanium alloy involves polishing surface of titanium alloy into isopropyl alcohol solution through ultrasonically, and then flushing by using super pure water and piranha solution.

SUN Z, WANG C, LI P, CHENG X, LIU Z

Preparation of transparent conductive graphene thin film used for e.g. organic light-emitting diode, by performing Hummers with carbon material, dispersing graphene oxide in organic solvent and substrate, and opening water groove.

FAN T, LIU Y, MIN Y, SONG J, TONG S, ZHANG L

Preparing large area multifunctional graphene thin film comprises ultrasonically dispersing graphite oxide in acidic solution, then adding conductive polymer monomer and oxidizing agent, and reacting and filtering mixture, then washing.

FAN T, LIU Y, MIN Y, SONG J, TONG S, ZHANG L

Flexible substrate processing apparatus used for reducing graphene oxide to form graphene comprises substrate carrying-out portion; reduction treatment portion; washing portion; drying portion; and substrate carrying-in portion.

TAKAHASHI M, SAITO Y, MOMO J, MORIWAKA T, KUSUMOTO N, MORIWAKA K, YONEDA Y

Preparation of carbonized film used for electrode material, involves adding 4,4'-diaminodiphenyl ether and benzophenonetetracarboxylic dianhydride into N,N-dimethylacetamide and adding graphene into obtained polyamic acid solution.

LI Y, NIU Y, WU J, ZHAO J