Preparing anti-ultraviolet fabric involves extruding graphene, adding into coagulation liquid, cooling, stirring, allowing to stand to solidify into graphene hydrogel film and mixing uniformly by receiving direct current electric field.

LIU H

Preparing graphene viscose composite fiber useful for composite fiber woven cloth, comprises e.g. pressing, stirring, heating, washing and drying, extruding and solidifying and electrospinning.

SONG H

Preparing graphene viscose composite fiber involves taking concentrated sulfuric acid, graphite, sodium nitrate in mass ratio, adding concentrated sulfuric acid to graphite and sodium nitrate in ice bath and stirring.

SONG H

Manufacture of corrugated paper for e.g. packaging electronic product, involves mixing titanium dioxide and graphene dispersion, degassing, spinning, drying, adding softwood fibers and alkyl ketene dimer, forming sheet and drying.

BI Q

Preparation of multifunctional graphene regenerated cellulose fiber for e.g. textile application, involves adding multi-layer graphene photocatalyst solution to cellulose solution, spinning using sodium sulfate and zinc sulfate.

LIU H, SONG J

Preparation of graphene-blended natural cellulose melt-blown nonwoven cloth involves processing sodium borohydride graphene solution, adding methyl methionine and wood pulp, heating, adding natural cellulose, extruding and spinning.

ZHOU W, LAI M, HUANG K, ZHOU S, XU J

Preparation of graphene cellulose blended nonwoven fabric used in textile fields, involves adding solution comprising potassium permanganate which is added until none of purple smoke generated by reacting with potassium permanganate.

CHOU W, LAI M, HUANG K, CHOU S, HSU C, CHOU W T, LAI M Y, HUANG K S, CHOU S H, HSU C Y

Preparing flame-retardant regenerated cellulose fiber involves preparing viscose spinning solution, preparing graphene-flame retardant dispersion, mixing graphene-flame retardant dispersion with viscose spinning solution.

CHEN H, DING K, LU P, MAO J

Preparation of antibacterial deodorizing regenerated cellulose fiber, involves dispersing graphene in water, adding nano titania, and dispersing, mixing with viscose spinning solution, and wet-spinning.

CHEN H, DING K, LU P, MAO J