High-strength conductive polyolefin composite material comprises hydroxyl-functionalized polyolefin, graphene, conductive carbon black, 1-pyrene butyric acid, tannic acid and additives.

WANG Z, WENG Y

Preparing modified carbon fiber reinforced phenolic resin composite by carrying out electroplating graphene oxide coating on carbon fiber fabric, soaking in ammonium molybdate/thiourea aqueous solution, hydrothermally reacting, soaking in phenolic resin and hot pressing.

WANG Z, GUO Z, MA J, LIU X, JIN L, LIU Y, AO Y

Preparing graphene-based composite phosphorus-based flame retardant used for imparting flame retardancy to flammable polymer, by performing surface modification treatment to graphene, preparing gel precursor, mixing modified graphene and sodium polymetaphosphate, vacuum-drying, crushing, and sieving.

HU G, LI C, FANG G, WANG Z, CHENG J

Conductive polylactic acid composite material comprises raw materials comprising polylactic acid and graphene oxide with haloalkane branched chains modified by silane coupling agent and loaded with nanometer zinc oxide, copper particles and silver particles on surface.

ZHU Y, JIANG H, WANG Z, LIU A, LI N, ZHENG J, CHEN Y, YANG Z, LUO Q, XIA M

Preparing thin-layer graphene polymer composite material comprises e.g. mixing and compacting e.g. polyvinyl alcohol, polyvinyl azide, ethylene-vinyl acetate copolymer, ethylene-methyl methacrylate copolymer, triallyl isocyanurate, epoxy resin, modified graphene, and 4,4'-diaminobiphenyl.

WANG Z

Preparing carbon fibers with biomimetic hierarchical interface layer comprises desizing carbon fibers, soaking in poly(ethylene glycol) bispyrene butyrate aqueous solution, drying, soaking with bispyrene butyric acid polyethylene glycol in graphene oxide aqueous suspension and drying.

WANG Y, LIU X, LIU Y, SUN H, LI P, WANG Z, GUO Z, JIN L, MA J, AO Y

Preparation of nano-carbon filler used for forming nano-carbon composite resin, involves dissolving nano-carbon powder after pre-processing in alkane solvent to obtain nano-carbon/alkane suspension, adding chlorosilane reagent to suspension, heat-reacting, cooling, filtering, and drying.

YANG W, WANG Z, XU L, LI X

Modifying highly dispersed amidated low-dimensional carbon material useful as macromolecule cross-linking agent comprises placing low-dimensional carbon in nitric acid, condensing, adding e.g. amidated modifier, ball milling and vacuum freeze-drying amidated low-dimensional carbon material.

WANG Z, WANG R, WANG X, MA Y, CUI S

Graphene modified rubber composite material used for tire tread comprises base rubber material, modified graphene material composed of graphene powder, polyvinyl chloride powder, vinyl acetate and talc, N,N-dimethylamide solution and water, vulcanizing agent and flow enhancer, and organic solvents.

HE Z, LIU Z, WANG Z, WU Q, FENG S

Wave-absorbing polyamide composite material for electronic products, e.g. television, comprises Fe3O4-graphene nano hybrid material is prepared by ferric chloride graphene sodium acetate and polyethylene glycol.

YI Q, WANG Z