Preparing anti-ultraviolet, anti-static, self-healing aqueous polyurethane modified graphene composite coating for leather, textile and wood, involves mixing and dispersing graphene oxide and nano-titanium dioxide in organic solvent.

DU W, LIN J

High-temperature resistant coating comprises polyester imine resin, cresol, polyol, isocyanate, graphene solution, stannous octoate, and xylene.

MA J, LUAN X

Preparation of amino-functionalized graphene modified polyurea long-lasting anticorrosive coating involves heating polyether polyol under inert environment, dehydrating, cooling, adding polyisocyanate, reacting, filtering and packaging.

WANG B, GUO Y, YUE C, WEN X, ZHANG T

Coating comprises functionalized graphene, isophorone diisocyanate, polyester polyol, catalyst, 1,4-butanediol, 2,2-dihydroxypropionic acid, leveling agent, and defoamer.

ZHU J

Graphene modified polyurethane superhydrophobic anticorrosive material includes modified graphene oxide, fluorinated hydroxyl terminated silicone oil, polyester polyol, 4,4'-diisocyanate-3,3'-di methyl biphenyl and 1,4-butanediol.

YANG J

Preparing graphene oxide modified aqueous closed isocyanate curing agent involves stirring and mixing the weighed graphene oxide, diisocyanate and methyl ethyl ketone to obtain a mixed solution A, and then heating in the reactor.

WU S, LI C, PAN C

Preparing graphene-based hybrid flame retardant useful in fields of intelligent packaging and coating, comprises e.g. adding graphene oxide and de-ionized water to three-necked flask, and adding commercial flame retardant solution.

JIN Y, YANG H, DU W, WANG S

Modified graphene waterborne polyurea resin used in aqueous polyurea coating, comprises isocyanate-modified sulfonated graphene which is first reacted with isophorone diisocyanate in organic solvent, and then with polyetheramine.

ZHANG J, WANG J, WEN S, ZHU Y, LI S

Preparing graphene modified flame retardant waterborne polyurethane coating and adhesive comprises e.g. adding ammonium molybdate, nano silver and 1,5-naphthalene disulfonic acid to terephthalic acid and deionized water and stirring.

DUAN B, WANG Q, WANG H, DIAO S, WANG X, LI X, TANG Z

Material used for manufacturing high-hardness coating for protecting aluminum alloy, comprises fluoropolyurethane polymer materials, organic solvents, graphene fluoride, and PTFE dispersion in preset mass ratio, and polyimide fibers.

JIANG G, TANG K, LI C, ZHAO Y, PENG M, ZHAN B