Preparing high performance polyvinyl alcohol/graphene composite film involves obtaining graphene oxide dispersion and polyvinyl acetate/graphene oxide solution, which is obtained by in-situ polymerization under nitrogen protection.

KOU S, DING K, XU L, ZHANG Y, LU R

Graphene-based PCB copper-clad plate, comprises copper-clad laminate prepreg, copper foil and prepreg, and a layer of chemical vapor deposited graphene between copper foils.

ZHANG J, ZHANG Y, XU Y, FENG S, WANG Q

Preparing graphene toughened resin-based carbon fiber composite material comprises e.g. ultrasonically dispersing graphene and the low-viscosity reactive dispersant, mixing dispersion with resin, drying, pressing and curing.

LIU L, LI A, PENG Y, ZHANG F, ZHANG Y, SHI L

Preparing graphene oxide grafted fluoropolymer by click using chemical synthesis comprises e.g. preparing graphene oxide, adding the graphene oxide into an anhydrous solvent and ultrasonically dispersing.

ZHANG L, XU L, ZHAI C, ZHANG Y, ZONG C, ZHANG S

Preparing graphene/polyamic acid conductive hydrogel involves dispersing graphene oxide in deionized water ultrasonically to obtain graphene oxide dispersion, adding hydrazine hydrate and ammonia water, and carrying out reduction reaction.

FAN W, WANG D, LIU T, ZHANG Y

Preparation of heat-resistant polyaniline conductive film involves adding heat resistant polymer to activated graphene dispersion, stirring, adding heat-resistant stabilizer, stirring and spin coating.

YANG Y, ZHANG Y

Oxidation-resistant conductive polypyrrole material comprises 2-mercaptobenzimidazole, antioxidant-modified pyrrole monomer, initiator, bisphenol A diglycidyl ether, polyamide wax powder, graphene, and zinc cyanurate.

YANG Y, ZHANG Y

Graphene amide dispersion is prepared by reacting zinc cyanurate, absolute ethanol, 2-benzimidazolethiol, polyamide wax micro powder, dimethylformamide, alcohol dispersion, bisphenol diglycidyl ether.

YANG Y, ZHANG Y

Preparation of reinforced polyimide composite material involves dispersing graphene oxide and carboxylated carbon nanotube in organic solution, adding N,N'-dicyclohexylcarbodiimide, dianhydride monomer and diamine monomer and molding.

SHI H, ZHANG Y, WANG H, YU W, LIU B

Preparing polyimide composite material involves dispersing graphene oxide and carbon nanotubes uniformly in water to obtain blending dispersion of carbon nanotubes/graphene oxide, adding dopamine hydrochloride, adjusting pH value.

SHI H, ZHANG Y, WANG H, MAO H