Long-life guide cylinder comprises e.g. outer layer as pre-oxidized felt insulating felt, middle layer as modified resin formed on inner side wall of outer layer, and inner layer as carbon/carbon composite material formed on inner side wall of middle layer.

BAI Y, QIN X, LIU Y, ZHOU J

High air salt concentration galvanized iron art railing forging processing technique involves heating iron rail, separating iron block impurity, immersing iron rail into the oil removing solution, and washing with deionized water.

SONG J

Coating structure for aging-resistant zinc-nickel alloy silane-free passivation, comprises aluminum alloy substrate, and chemical deposition zinc layer, chemical nickel plating layer, and silane chromium free passivation layer.

CHEN J, GUO C, LAI H

Corrosion prevention composition for metal substrate, comprises sacrificial metal particles, where sacrificial metal particles comprise metal selected from nickel, molybdenum, or cobalt, and sacrificial metal particles are not passivated.

HAWKINS T, VIRTANEN J A

Surface modified copper bus bar, has lapping surface and non-overlapping surface of copper bus are attached with silver bottom layer by magnetic control sputtering technology.

LIN Q, MEI Z

Preparing Teflon corrugated pipe internal crimping joint comprises using 304 stainless steel processing to make withholding joints and coating crimping joint surface with corrosion-resistant modified polyperfluoroethylene propylene coating.

WANG W, WANG L, LI S

Preparation method of guardrail with good corrosion resistance by subjecting base material to vortex flaw detection, removing rust, hot-dip galvanizing, passivating and degreasing, phosphating, drying, spraying zinc-rich primer and curing.

ZHANG X

Plastic spraying method for structural portions of lamps, involves using surface treatment process and subsequent spraying process, where the treatment process includes degreasing sub-process and sub-process includes film forming process.

CHENG A, XU L, GUO H, LI S

Preparing anode foil by heating and treating corroded foil, using forming solution for perform forming of corroded foil, coating graphene solution on surface of forming foil, sintering and performing phosphating treatment on forming foil.

LIU G, HUANG H, WU Q, HUO J, OU K, CHEN Y, FENG Z, YANG F

Combined use of coating and impressed current cathodic protection technology for metals, by coating primer layer, conductive coating and topcoat layer on metal surface, and connecting to negative and positive electrodes.

DENG P, HU J, WANG G, LIU W, HUANG H