Preparation of highly thermally conductive insulating grease filled with modified graphene microdisk involves preparing cyanide graphene microchip, mixing with coupling agent hydrolysate, mixing with dimethyl silicone oil, and roasting.

JIANG H, LUO Z, LIN Q, LIN H

Carbonyl iron/graphene/polyvinylpyrrolidone composite microwave absorbing material useful for preparing microwave absorbing sheet, comprises carbonyl iron powder core layer, graphene layer and polyvinylpyrrolidone layer.

SUN X, WENG X, ZHANG Y

Preparing polythiophene/graphene/attapulgite conductive composite for manufacturing antistatic coating, involves weighing graphene and attapulgite, adding graphene oxide into aqueous ethanol solution, and dispersing ultrasonically.

ZHANG Z

Zinc-ferrite-silica-graphene absorber for e.g. electromagnetic wave shielding material, comprises zinc-ferrite-silica-graphene ternary complex containing composite of magnetic loss-type zinc ferrite, graphene and silica, and paraffin.

LI L, FENG J, HOU Y

High thermal conductivity type epoxy resin composite material for LED bonding layer, contains bisphenol A type epoxy resin, boron carbide powder, aluminum oxide, glue 107, dibutyltin dilaurate, ethyl orthosilicate, graphene oxide.

LI H, LIU Y, CHEN Y

Preparing graphene-based thermally conductive interface material comprises mixing graphene material, vinyl silicone rubber, hexagonal boron nitride, vinyl silicone oil and first silane coupling agent, compressing, rolling and cutting.

DING S, ZHOU X, LIU Z

Preparing magnesium oxide-graphene composite heat-conducting insulating filler involves adding an aqueous magnesium salt solution to the aqueous solution of graphene oxide and adjusting pH value.

FENG J, CHEN Z, LU Q

Polyvinyl alcohol-graphene oxide crosslinked polymer-coated modified nano calcium carbonate powder useful as filler, contains calcium oxide, carbon dioxide, sodium lignosulfonate, polyvinyl alcohol, and glutaraldehyde aqueous solution.

WANG W

Graphene-containing silicon rubber thermal-interface material used for LED, contains silicone rubber matrix, aluminum nitride, dopamine, silver nitrate solution, hydroxysilicone oil, vulcanizing agent, graphene and sodium dodecyl sulfate.

XIA Y