Making porous graphene thin film involves mixing graphite powder and 1-methyl-2-pyrrolidone to form graphene dispersion liquid, and then performing electrostatic spraying and substrate heating method on silicon substrate to obtain film.

CHEN L, YANG S, ZHANG Z, ZHAO J, ZHENG H

Preparation of graphene oxide modified polyacrylonitrite carbon fiber precursor comprises dispersing graphene oxide in solvent, uniformly performing ultrasonic dispersing, preparing spinning original solution, and spinning original liquid.

LV Y, GONG N, LU Y, YAO L

Complex fiber useful in preparing impact resistance material and/or vibration-absorption material e.g. bulletproof material, comprises ultra-high molecular weight polyethylene and graphene.

GAO P, HE J, HUANG Y, LU G, MA T, MA Y, ZHANG H, ZHANG J, ZHANG T

Production of polyacrylonitrile graft graphene macro fiber used as high strength fiber, comprises mixing graphene or oxidized graphene, and initiator, adding polyacrylonitrile graft of graphene, and processing solidification filamentation.

GAO C, LIU Z

Method for preparing graphene/polyacrylonitrile composite carbon fiber, involves adding oxidized graphene with solvent, acrylonitrile monomer and initiator and heating, followed by reacting under protection of nitrogen and depositing.

GAO C, LIU Z

High intensity orderly arranged porous graphene fiber, useful for loading various types of catalysts, and as lightweight wire, prepared by e.g. reacting graphite and sulfuric acid, filtering, drying, stirring, and ultrasonically treating.

GAO C, XU Z

Preparation of graphene/polyimide composite fiber involves adding graphene or graphene oxide to polyamic acid solution to obtain graphene/polyamic acid spinning stock solution, polycondensing, and wet spinning or dry spraying wet spinning.

CHEN D, DONG J, WANG Y, ZHANG Q, XIA Q, YIN C

Preparation of graphene-modified polyacrylonitrile-based carbon fibers used for e.g. electrical conductive material, involves mixing graphene suspension and polyacrylonitrile solution, performing spinning process oxidizing and carbonizing.

CHEN Y, MA H, OUYANG Q, YANG J, MO G, HUANG X

Ion reinforced graphene fiber prepared by mixing graphite and sulfuric acid, cooling, filtering, drying to obtain intercalated graphite, mixing with e.g. sulfuric acid, filtering, ultrasonically treating obtained graphene oxide, and drying.

GAO C, XU Z

Vapor phase epitaxy carbon fiber assembly used as electrode material of lithium cell, is aggregate of vapor growth carbon fiber having tubular graphene layer structure, and average fiber outer diameter in preset range.

HITOE Y, SUZUKI J, SATO H, KAWASHIMA S, SUZUKI A