国家/地区 中国（12）
IPC部 C（12）
IPC大类 C08（12） D01（12）
IPC小类 C08G（12）
IPC D01F001/09（12）
发明人 DONG H（2） HAO C（2） HU C（2）
HU S（2） JIANG J（2） LAI G（2）
MA Q（2） PAN Q（2） WANG X（2）
公开年 2017（6） 2018（6）
申请年 2017（12）
专利权人 UNIV HANGZHO.（2） ZHEJIANG HEN.（2）

Preparing conductive polyethylene terephthalate fiber comprises e.g. mixing graphene oxide, conductive carbon black and ethylene glycol, adding terephthalic acid and stabilizer, and carrying out high temperature esterification reaction.

LI N, FAN Y, PAN X, PANG D

Hydrophilic antistatic graphene modified polyester chip, prepared by esterifying, adding catalyst, performing polycondensation reaction and performing underwater pelletizing.

HU S, WANG X, HU C, DONG H

Preparation of modified polyamide composite fiber, involves adding hexamethylenediamine and polyphosphoric acid to water, stirring, adding graphene into water, ultrasonically dispersing, leaving still, cooling, filtering, and drying.

MAO Z

Catalyst loaded graphene modified polyester comprises graphene powder or graphene oxide powder loaded with catalyst, ethylene glycol, and terephthalic acid , and obtained by esterification and polycondensation reaction.

HU S, HU C, DONG H, WANG X

Preparation of highly dispersed graphene-nylon 6 composite fiber, involves carrying out micro mechanical peeling of graphite into graphene in aqueous solution of caprolactam to obtain graphene-caprolactam aqueous solution.

ZHANG G, XU Y, CHEN Y, TANG L, WU G

Preparing biomass graphene-spandex composite fiber by mixing methylene diphenyl diisocyanate and polybutylene glycol, polymerizing, adding textile additive and mixing spandex filament stock solution with graphene and coupling agent.

XU L

Preparation of graphene-polyester conductive polyester filament for screen printing, involves adding nano-graphite powder, ethylene glycol and organic solvent, adding catalyst and stabilizer, heating, stirring, dispersing, and heating.

YAO X, XU G, TANG Y

High content graphene modified nylon 6 masterbatch used in manufacturing of thermally conductive, conductive nylon composites and permanent antistatic nylon 6 fibers or permanent antistatic nylon 66 fiber, comprises caprolactam.

CHEN R, CHEN X, DENG K

Preparation of polyoctahedral silsesquioxanes graft graphene oxide modified nylon composite resin used e.g. electromagnetic protective clothing includes dissolving graphene oxide in deionized water and ethanol, reacting, cooling and molding.

HAO C, LAI G, JIANG J, PAN Q, MA Q, LI Z

Preparation of graphene oxide-modified copolyesteramide and its fibers used for electromagnetic and electrostatic protective clothing involves mixing polymerizing caprolactam with graphene oxide, and melt-spinning in twin-screw extruder.

HAO C, LAI G, PAN Q, JIANG J, MA Q, LI M, LUO M